Hysol®Huawei KL1000-3NP™ epoxy molding compounddelivers outstanding performance and ease of use
.Huawei KL1000-3NP™ meets UL 94 V-0 Flammability at3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 20Spiral Flow, @ 175°C, cm 75Shelf Life:@ 5oC, months 12TYPICAL PROCESS DATAHandling
Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 18Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 40 to 100Automold, seconds 40 to 80Post Cure @ 175°C, hours 4 to 6Huawei KL1000-3NP™ has been formulated to provide the bestpossible moldability and as wide a molding latitude as possible.Although molding and curing conditions will vary from situation to ituation, recommended starting ranges are shown above.TYPICAL PROPERTIES OF CURED MATERIALAll measurements taken at 25 °C unless otherwise noted.
All physical,electrical and analytical measurements taken on specimens curedfor 2 minutes @ 175 °C with post cure of 6 hours at 175 °C, unlessother wise specified
Hysol®HuoliKL1000-3NP™環(huán)氧樹(shù)脂成型復(fù)合材料具有出色的性能和易用性.Huawei KL1000-3NP™符合UL 94 V-0可燃性，厚度為3.7575mm。
固化材料的典型特性時(shí)間@ 175°C秒秒20螺旋流@ @ 175℃，厘米75Shelf壽命：@ 5℃，月12工藝流程數(shù)據(jù)處理預(yù)熱溫度：常規(guī)模具，°C 80至100Automold，秒0至5模具溫度，℃150至195壓鑄壓力，Kg /cm240至100轉(zhuǎn)印時(shí)間：常規(guī)模具秒10至18Auold，秒4至10℃，@ 175℃：常規(guī)模具，秒40至100Automold，秒40至80后固化175℃，小時(shí)4至6Huawei KL1000-3NP™已經(jīng)配制，以提供盡可能*佳的可模塑性和寬的成型緯度。
盡管成型和固化條件將變化從情況到情況，推薦的啟動(dòng)范圍如上所示。
固化材料的特性所有測(cè)量在25°C下進(jìn)行，除非另有說(shuō)明。
所有物理，電學(xué)和分析測(cè)量在175℃下固化2分鐘，175℃下固化6小時(shí)，除非另有規(guī)定 |