Teroson EP 1450
TEROSON EP 1450 is an expanding one component, high strength structural foam based on Epoxy. The non cured material is resistant to washing and phosphating solutions in normal use in automotive industry and to electro dip painting. The final part gets its geometric shape i.e. by injection molding. TEROSON EP 1450 will cure while passing the EC-oven.
APPLICATION AREAS
TEROSON EP 1450 must be applied as a preformed part in the body shop. The material increases stiffness, strength, fatigue limits and vibration behavior of vehicle bodies. The part is clipped into hollow cavities.
TECHNICAL DATA
(Typical Test Results)
Uncured
Colour grey
Consistency solid
Density at delivery approx. 1.3 g/cm3
Solids Content
(3 h, 105 °C)
> 99 %
Cured
Recommended curing conditions:
mini: 15 min 155°C (keep)
maxi: 20 min 195°C (keep)
Density after expansion approx. 0.6 g/cm3
Expansion > 100 %
Compression test
Compressive strength > 10 MPa
Compressive modulus > 450 MPa
Lap shear strength
Substrates galvanized steel
Bonding area 20 x 25 mm
Layer thickness 2 mm
Strength > 2 MPa
Glass transition
temperature range
(Tg) DMTA (40 Hz, 2 K/min)
> 100 °C
Corrosion resistance
Salt spray test
(35 °C, salt solution 5 %,
500 hours)
no corrosion, no loss of adhesion
Corrosion test (VDA 621-415) no corrosion, no loss of adhesion
Water absorption
(24 h, 98 % humidity, 40 °C)
< 0.5 % weight increase
In service temperature -30 to 80 °C
泰羅松EP 1450是一個擴展的一個組成部分，基于環(huán)氧樹脂高強度結(jié)構(gòu)泡沫。非固化材料對汽車行業(yè)的清洗和磷化液具有良好的耐腐蝕性，可用于電涂漆。*后一部分得到其幾何形狀，即注塑成型。泰羅松EP 1450治愈而通過EC爐。
應(yīng)用領(lǐng)域
泰羅松EP 1450作為預(yù)留部分美體小鋪。該材料增加剛度，強度，疲勞極限和振動行為的車身。該部件被夾在空心空腔中。
技術(shù)數(shù)據(jù)
（典型測試結(jié)果）
未固化的
顏色灰色
一致性固體
密度約1.3克/厘米3交貨
固體含量
|
免責(zé)聲明：以上所展示的信息由會員自行提供，內(nèi)容的真實性、準(zhǔn)確性和合法性由發(fā)布會員負責(zé)，www.qy6.com對此不承擔(dān)任何責(zé)任。如有侵犯您的權(quán)益，請來信通知刪除。