TEROSON EV 6152 HDF is an EVA based thermoplastic material. Its primary function is to be designed in for use as an integral damping component at, or near, vibratory sources to dissipate energy through the transmission path. TEROSON EV 6152 HDF is a viscoelastic expandable, high damping foam exhibiting material damping loss factor above 1.1 in the targeted frequency range. Damping of
structure borne noise sources such as:
- Engine
- Suspension
- Exhaust system
- Accessories drives
APPLICATION AREAS
Closure panels, Hollow body network, Doors, Frame, Hoods, Engine and suspension cradles, Deck lids, Unibody network.
TECHNICAL DATA
(Typical Test Results)
Colour anthracite
Consistency solid
Odour weak, characteristic
Expansion > 450 to 700 % (depending on
sample dimension and curing
conditions)
Density at delivery 1.19 to 1.21 g/cm3
Corrosion resistance
on electro coated steel * no corrosion
on bare steel * no corrosion
Shear strength 0.3 to 0.5 MPa
layer thickness 3 mm
curing conditions 15 min at 175 °C
(object temperature)
In service temperature range -40 to 80 °C
480h 500ml/h 5% NaCl-solution / 35°C according to VDA 621-415
泰羅松EV 6152 HDF是基熱塑性材料的伊娃。它的主要功能是設計用于作為一個整體的阻尼組件，或附近，振動源的能量耗散通過傳輸路徑。泰羅松EV 6152 HDF是一種粘彈性可擴展、高阻尼聚氨酯泡沫材料的阻尼損耗因子在1.1以上的有針對性的頻率范圍。阻尼
技術數(shù)據(jù)
（典型測試結果）
顏色無煙煤
一致性固體
氣味微弱，特征
擴展> 450到700%（取決于
試樣尺寸和固化
條件）
密度1.21克/厘米1.19交付3
耐腐蝕性
電鍍層鋼無腐蝕
裸鋼無腐蝕
剪切強度0.3至0.5兆帕
層厚度3毫米
固化條件15分鐘在175°C
（物體溫度）
在服務溫度范圍- 40至80°C
480h 500ml／h 5%的NaCl溶液/ 35°C根據(jù)VDA 621-41 |